1, The film has good physical, chemical, and mechanical properties.
2, The film is smooth, easy to polish, easy construction.
3, And the bottom, the finish are good between the binding force, can increase the gloss and fullness of the finish.
4, Can be
From the modified acrylic resin polymer and the constant yellow polyisocyanate hardener anti-rust paint and filler refined from the two-liquid type primer.
Glass and steel products, oilfield equipment, bridges, steel racks, storage tanks, factory equipment and other steel structures used in the anti-corrosion with midway paint.
Color Gray, light yellow, other designated colors.
Hiding power 12m2 / kg or more
Specific gravity 1.1kg / L or more
Viscosity coated 4 # cup, 100 ± 5s
Drying time Refers to touch: 30min or less: 3h hardening: 24h (25 ℃)
Film thickness Dry film: 30 ~ 50μm
Theoretical coating Amount of 12m2 / kg
Painting interval At least 8h or more
Mixing ratio Main agent Paint: Curing agent = 5: 1
Applicable primer PY series at room temperature from dry primer.
Storage stability Under normal circumstances, at least one year.
Painting method Brush, air spray, airless spray, electrostatic spray.
1,The main agent paint and hardening agent must be in accordance with the provisions of the proportion of uniform blending, and spent within the specified time.
2, The surface of the coating of water, grease, dust and other dirt should be removed clean.
3, Dilution should use a special diluent to prevent the occurrence of bubbles or pinholes.
4, Hardener because it is easy to react with the water in the air to produce bubbles and gelatinization, the lid must be tightened to prevent contact with moisture in the air.
5, A spray thickness of more than 50μm, easy to produce bubbles. Construction should be effective control.
The actual coating amount of the paint is changed according to the size of the painted material, the working environment. The general loss factor is 1.4 times of the theoretical brush, and the coating is 1.7 times the theoretical coating amount.