1, Room temperature from dry, low temperature baking general topcoat.
2, High gloss, smooth surface appearance, with superior adhesion and hardness and wear resistance.
3, Good weather resistance, durable does not change color, without losing the light
By the import of hydroxy acrylic resin and non-constant yellow polyisocyanate hardener, imported light-resistant paint refined from the two liquid-type drying at room temperature and low-temperature baking dual-use colored finish.
Vehicles, high-grade construction machinery, oil field equipment, high-grade metal products, steel and wood products of colored finish.
Color Color Gloss: 92% or more Hiding power: 12m2 / kg or more
Fineness Below 20μm Hardness: ≥2H
Specific gravity 1.1kg / L or more Bending: 2mm Impact strength: 50kg.cm
Baking time 70 ℃ 40 minutes 80 ℃ 30 minutes
Dry at room temperature Refers to contact 30 minutes dry 8h hard dry 24h detection: 48h
Water-resistant Immersed in distilled water for 240h, do not blister, do not fall off, allowing a slight discoloration, loss of light.
Resistant gasoline 4h, do not blister, do not fall off.
Applicable Primer PY Series All Primers, Medium Paint.
Storage stability Under normal circumstances, at least one year.
Painting method Brush, air spray, airless spray, electrostatic spray.
1, Before use must be fully stirred evenly. If the paint is too thick, it can be diluted with diluent, but not more than the amount of the principle.
2, The surface of the coating of water, grease, rust, sludge, damaged or loose paint and corrosive salts, etc., attached to the dirt must be cleaned to ensure that the paint protection.
3, The surface of the wet condensation of dew or in rainy days, and the temperature is too high (40 ℃ above) or too low (0 ℃ below), should avoid construction.
4, Do laminated coating, you must wait for the underlying film is completely dry before construction.
The actual coating amount of the paint will change according to the size of the painted material, the working environment, the general loss factor: the hand brush for the theoretical coating amount of 1.4 times; spray for the theoretical coating of 1.7 times the calculation.