1, Excellent resistance to mechanical wear.
2, Oil resistance, chemical resistance and excellent anti-rust performance.
3, The film tough and excellent adhesion and laminated.
4, Wear resistance, excellent grinding type.
Two liquid type primer which is refined from epoxy resin, amine type curing agent advanced pigment and filler.
Vehicles, engineering machinery, bridges, steel racks, storage tanks, oilfield equipment, factory facilities and other steel structures used in the anti-rust, anti-corrosion with half-way primer.
Color Gray, light yellow, other specified color.
Gloss 5-10% Pencil Hardness: ≥HB
Hiding power 12m2 / kg or more Adhesion: Level 1 (grid)
Specific gravity 1.15kg / L or more
Viscosity coated 6 # cup ≥ 75s
Dry time refers to touch: 40min or less dry: 4h hard dry: 24h
Drying time 70 ℃ 40min
Film thickness Wet film: 85 μm Dry film: 45 μm
Theoretical coating capacity 14 m2 / L 12 m2 / kg
Painting interval At least 8h
Solid content More than 65%
Mixing ratio Main agent Paint: Curing agent = 5: 1 (weight ratio)
Diluent Epoxy diluent
Diluent dosage 10-25%
Applicable primer PY series at room temperature from dry primer.
Applicable topcoat PY series at room temperature from dry finish.
Storage stability Under normal circumstances, at least one year.
Painting method No air spray, air spray, electrostatic spray.
1, Before use must be fully stirred evenly. If the paint is too thick, it can be diluted with diluent, but not more than the amount of the principle.
2, The surface of the coating of water, grease, rust, sludge, damaged or loose paint and corrosive salts, etc., attached to the dirt must be cleaned to ensure that the paint protection.
3, The surface of the wet condensation with dew or rainy days, should avoid construction.
4, Do laminated coating, you must wait for the underlying film is completely dry before construction.
The actual coating amount of the paint will change according to the size of the painted material, the working environment, the general loss factor: the hand brush for the theoretical coating amount of 1.4 times; spray for the theoretical coating of 1.7 times the calculation.