1, The surface of the coating without too strict surface treatment.
2, The film is tough and full of flexibility and adhesion. The
3, Oil resistance and solvent resistance and excellent chemical resistance.
4, Excellent wear resistance, water resistanc
From epoxy resin and amine hardener, together with high-grade zinc powder rust-resistant pigments and fillers refined from the durability of rust, heavy anti-corrosion two-type primer.
Chemical plants, bridges, steel frames, storage tanks, oilfield equipment and other steel structures attached to the use of high rust, heavy anti-corrosion primer.
Solid Content ≥ 80%
Fineness 45μm Adhesion: Class 1 (grid) Flexibility: 2mm
Drying time Refers to: 60 minutes dry: 18 hours hardening: 48 hours
Water resistance (168h) does not blister, do not rust, do not fall off.
Oil resistance (48h) no significant change in appearance.
Salt resistance (1000h) Uncut line, through the first, (600h) cutting line side 2mm, through a level
Pencil hardness ≥ 2H impact strength ≥ 50kg, ㎝
Mixing ratio Main agent Paint: Curing agent = 10: 1 (weight ratio)
Applicable topcoat PY series at room temperature from dry paint, finish.
Storage stability Under normal circumstances, at least one year.
1, The main agent paint and hardening agent must be in accordance with the provisions of the proportion of uniform blending, and spent within the specified time.
2, The surface of the coating of water, grease, dust and other dirt should be removed clean.
3, Dilution should use a special diluent to prevent the occurrence of bubbles or pinholes.
4, Hardener because it is easy to react with the water in the air to produce bubbles and gelatinization, the lid must be tightened to prevent contact with moisture in the air.
5, A spray thickness of more than 50μ, easy to produce bubbles. Construction should be effective control.
The actual coating amount of the paint is changed according to the size of the painted material, the working environment. The general loss factor is 1.4 times of the theoretical brush, and the coating is 1.7 times the theoretical coating amount.