1, The surface of the coating without too strict surface treatment.
2, The film is tough and full of flexibility and adhesion.
3, Oil and solvent resistance and excellent resistance to chemicals.
4, Excellent wear resistance, water and sea resistance i
From epoxy resin and amine hardener, together with mica iron oxide and rust-resistant paint, filled with exquisite durability of rust, heavy anti-corrosion two-type paint.
Chemical plants, bridges, steel racks, storage tanks, oilfield equipment and other steel structures with high adhesion to the use of rust, heavy corrosion with the paint.
Color Iron red, iron gray. Adhesion: ≤1 (grid)
Hiding power 12m2 / kg or more Impact resistance: 50kg.cm
Specific gravity 1.5kg / L or more Hardness: ≥ HB
Viscosity coating # 6 cup ≥ 75s resistant to bending: 2mm
Drying time Refers to touch: 30 minutes or less dry: 2 hours hardening: 24 hours
Film thickness Wet film: 70 μ dry film: 40 μ
Theoretical coating Amount 15 m2 / L 12 m2 / kg
Painting interval 60 days at any time to do the stack or recoat
Applicable topcoat PY series at room temperature from dry finish.
Storage stability Under normal circumstances, at least one year.
Painting method Brush, airless spray, air spray, electrostatic spray.
1, Before use must be fully stirred evenly. If the paint is too thick, it can be diluted with diluent, but not more than the amount of the principle.
2, The surface of the coating of water, grease, rust, sludge, damaged or loose paint corrosive salts and attached dirt must be cleaned to ensure that the paint protection function.
3, The surface of the wet condensation with dew or rainy days, should avoid construction.
4, Do laminated coating, you must wait for the underlying film is completely dry, before the construction.
The actual amount of paint will be changed according to the size of the painted material, the working environment, the general loss factor: hand brush for the theoretical coating of 1.4 times the amount of coating for the theoretical coating of 1.7 times the calculation.