1, With good physical and mechanical properties, good adhesion.
2, With corrosion resistance, oil, water, acid, alkali, salt and other chemical media corrosion.
3, Low resistivity, with good anti-static capacity.
It is made of high-grade modified epoxy resin special plasticizer, conductive pigment, anti-rust paint and other modified amine curing agent composed of two-component anti-static anti-corrosion coating.
Applicable to crude oil tank, tank and oil pipeline within the anti-static requirements of the equipment long-term anti-corrosion.
Flexibility .mm ≦ 2
Impact strength kg.cm 50
Adhesion level 1
Drying time (25 ℃) Table dry 3h dry 24h
Surface resistivity ≦ 4 × 108
Volume resistivity ≦ 3 × 107
Resistant to hydrochloric acid (10%, 25 ℃) 30d no change
Resistant gasoline (25 ℃) 180d no change
Alkali resistance (25%, 25 ℃) 60d no change
Salt resistance 100h no change
Painting method Brush, spray
Curing agent ratio 5: 1 = the main paint: curing agent
Diluent Epoxy diluent
Diluent dosage 10-20% (without cleaning tool)
1, The product should be kept in the storage of ventilation, dry, to prevent direct sunlight, and should be isolated from the source of heat from the heat source, the summer temperature is too high to try to cool.
2, The product is transported, should prevent sun exposure, rain, and should comply with the relevant provisions.
3, The product in line with the provisions of 1,2 storage conditions, since the date of production, the effective storage period of one year, more than the validity period can be tested according to the provisions of this standard, after passing can still be used.
Paint brush coating for the theoretical coating of 1.4 times: spray for the theoretical coating of 1.7 times the calculation.