1, On the special treatment of a variety of nylon substrate has a good adhesion.
2, High hardness, good water resistance.
3, With other topcoat good compatibility.
It is composed of modified acrylic resin and non-yellowing polyisocyanate hardener with refined, pigment, filler, silicone adhesion promoter, other additives and organic solvent.
Applicable to all kinds of nylon substrate coating.
Color Color, in line with the model color
Paint film appearance Smooth
Original paint fineness ≤ 20μm
The original paint viscosity 60 ~ 80s (coated -4 viscometer) / 25 ℃
Adhesion 100/100 level (crossed stripping method)
Dry time table dry ≤ 20min hard work ≤ 8h (room temperature)
Hardness ≥H (pencil method)
Construction ratio The main paint: curing agent: thinner = 10: 3: 4-6 (weight ratio)
Water resistance 48h does not blister, do not fall off with acrylic polyurethane finish, covered with varnish, do not bite the bottom, do not fall off, excellent adhesion
1, Before the construction, the paint should be fully stirred, according to the paint: curing agent: the proportion of diluent mixture, after 200 mesh screen filter before construction, construction viscosity (coated -4 viscometer) 13 ~ 15s is appropriate.
2, The use of wet wet process is better, for two construction, the first and the second road separated by 30 minutes is appropriate.
3, The workpiece after a good spray, leveling about 10 minutes into the oven at low temperature 60 ℃ bake 30 minutes or room temperature drying 24 hours can be packaged.
1, Before nylon plastic coating, with xylene or thinner to remove the surface of the oil, release agent, dust and other impurities, and remove static electricity.
2, Do not mix with water and other oil, so as not to affect the paint performance.
3, The original paint are flammable, can not be close to the fire, construction, should maintain a good ventilation environment.