1, The film shiny high, good transparency, feel smooth.
2, Good film fullness, high hardness, good leveling.
3, The film has excellent corrosion resistance, water degradation, chemical resistance, wear resistance.
By the import of high-grade acrylic resin, curing agent with a special import additives refined from the two liquid-type transparent finish
It is suitable for semi-light nickel drawing and electroplating workpiece painting on plastic substrate
Pencil hardness ≥H (detected on bulk substrate)
Adhesion 100 Lattice test 5B (detected on bulk substrate)
Abrasion resistance 12 Liters of sand test, no breakdown phenomenon (in the body substrate detection)
Water resistance 38 ℃ in distilled water for 24 hours, no abnormal paint.
Corrosion resistance CASS 8 hours or more, the film surface without corrosion or discoloration and other defects (on the body substrate detection)
Hot and cold cycle ①-40 ℃, 20min ② 20 ℃, 20min ③ 75 ℃, 20min ④20 ℃, 20min, a total of 4 cycles, the coating without skin and off the phenomenon (on the body substrate detection)
Chemical resistance 6N Ammonia, 6N sodium hydroxide, 100% methanol, 6N hydrochloric acid and 100% detergent each two drops on the surface for 16 hours, no discoloration, peeling and other defects (detected on the bulk substrate)
Construction method Air spraying or electrostatic spraying (special electrostatic thinner required)
Construction ratio Light varnish: Special curing agent: Dedicated diluent = 2: 1: 1-1.5 (weight ratio)
Construction Viscosity Lwata 2 # Cup 12-15s (25 ℃)
Drying time 70 ℃ Bake drying 40min-60min room after room temperature for 72h measured its properties, chemical properties
Before use, please stir evenly, with a good paint after standing for 10 minutes, with 200 mesh sieve after use, to use the company's ancillary products, open the cover after the paint is not used to seal, mixed paint as much as possible in the 4 hours run out, how much with the number of paint to avoid waste.
This product contains flammable and explosive volatile solvents, to avoid fire and skin contact, the site to maintain good ventilation.